Technical Data Sheet - PR1010 Coating


PR1010 is a heat cured, flat black modified phenolic resin coating, which exhibits outstanding properties in the areas of:

  1. Corrosion Resistance
  2. Abrasion Resistance
  3. Chemical Resistance
  4. Versatility
  5. Low Outgassing

PR1010 is applied by spray coating the part, the typical coating thickness is 0.0005". 

The coating retards oxidation of the base material and is not meant to provide impact protection.

The recommended Maximum Operating Temperature of this high performance coating is 392F (200C).

Typical Functional Performance

Pencil Hardness

3H

Taber Abrasion

(CS-10 Wheel, 1 kg. Load, ASTM D-1044, D-51)

12.2 mg/1000 Cycles

Corrosion Resistance

Salt Spray, ASTM B-117 (Steel Q-panels, zinc phosphate, .5 mil film thickness, nominal)

500 Hours +

Fluid Resistance
(ASTM D-2510C)

Standard Test Fluid TT-S-735, Type II

Pass

Aviation Gas, MIL-G-5572, Grade 115/145

Pass

Hydraulic Fluid, MIL-H-5606

Pass

Methyl Ethyl Ketone

Pass

Aircraft Lube Oil, MIL-L-6082 Grade 1100

Pass

Aircraft Turbine Oil, MIL-L-7808

Pass

H-D Lube Oil, MIL-L-2104, Grade 10

Pass

Non-petroleum Hydraulic Fluid, MIL-H-8446

Pass

Trichloroethylene, O-T-634 DC-550 Fluid

Pass

1,1,1-Trichloroethane

Pass

Outgassing Characteristics

(ASTM E 595) Total Mass Loss (TML)%

1.50

Collected Volatile Condensable Material (CVCM)%

0.04

Total Water Vapor Regained (WVR)%

0.70

TDS: PR1010 Rev 3 (10/21/2008)